Alloy 910 HDT, High temperature 112C HDT
Taulman3D’s Alloy 910 is a measurable advancement in 3D Printing materials technology from taulman3D. taulman Alloy 910 is the combined effort of chemical companies, extrusion manufactures and taulman3D to specifically develop a single material to meet as many high performance 3D Printing needs as possible. And Alloy 910 HDT continues those features but with a higher HDT for even higher temperature requirements.
Specifications:
Tensile Strength = 8,100PSI
Modulus PSI = 72,932
Max Elongation at break = 31%
Print Temperature = 285C - 300C
Nozzle size = Any - There are no particulates or additives in Alloy 910
HDT = 112C and > 150C when annealed
Print Bed =
Cold = BuildTak with coat of gluestick
Hot = Glass heated to 55C with coat of PVA
(PVA is 50% water and 50% Elmers Glue All)
Shrinkage = 0.0033 in/in
Nylon 230 ist das erste Nylon Filament von Taulman, das bei 230 ° C oder weniger verarbeitet wird. Dies ist eine niedrigere Temperatur als jedes andere Nylon-Filament für deinen ...
PA cast Plate Nylon High Strength 95MPA, High temperature 110C HDT
Taulman3D’s PA Cast Plate is a High strength poly-amide that uses manufacturing techniques similar to Nylon industrial plates. Casting ...
Alloy 910 HDT, High temperature 112C HDT
Taulman3D’s Alloy 910 is a measurable advancement in 3D Printing materials technology from taulman3D. taulman Alloy 910 is the combined effort of chemical ...
910 ist die erste 3D-druckbare Co-Polymer-Legierung mit hoher Schlagzähigkeit und Haltbarkeit, die eine Zugfestigkeit von 8.100PSI aufweist und damit 10-15% glasgefüllten Materialien entspricht! Alloy 910 ist für Anwendungen bei ...